A fibril-inducing support-bath enables embedded 3D printing of aligned collagen-rich constructs

Embedded extrusion printing can process collagen-rich bioinks, but their low viscosity and slow fibrillogenesis compromise print fidelity and post-deposition stability. Here, we developed a collagen fibril-inducing support bath (FIB) that combines mechanical support for embedded printing with biochemical induction of collagen assembly. Microfibrillated or nanofibrillated cellulose was incorporated into a fibril-inducing buffer, and formulations were screened at 37 °C for rheological behaviour and optical transparency. The selected FIB was evaluated by printing 1% and 5% (w/v) articular cartilage-derived extracellular matrix (ECM) inks at 10–20 mm s□¹ and compared with a cellulose-only control bath. FIB exhibited yield-stress, shear-thinning and rapid recovery behaviour that supported reproducible filament deposition. Unlike the control bath, FIB enabled intact construct retrieval following stabilisation and promoted the formation of fibrillar collagen within the printed strands. Scanning electron microscopy revealed D-banded collagen fibrils preferentially oriented along the deposition direction, with dominant orientation peaks within ±10–15°. The platform supported the fabrication of 15 × 15 × 1.5 mm sheets and 6 × 6 × 6 mm scaffolds whose macroscopic dimensions were retained after processing. Constructs produced from 5% ECM inks exhibited approximately fourfold higher ramp and relaxation moduli than those produced from 1% ECM inks. Extracts from both formulations caused no detectable reduction in cell metabolic activity after 24 or 72 h. Mesenchymal stem/stromal cells (MSCs) seeded onto printed sheets became markedly elongated and aligned by day 3, with approximately 80% of cells having an aspect ratio exceeding 1.5, significantly greater than cells seeded onto casted ECM controls, with a mean deviation of ∼9° from the filament print direction. These findings establish FIB as a bioactive support bath that couples embedded printability with collagen fibrillogenesis, enabling recoverable collagen-rich constructs with aligned fibrillar architecture that directs early cellular organisation.