Exploring the Relationship Between Electrical Characteristics and Changes in Chemical Composition and Structure of OSG Low-K Films Under Thermal Annealing

Read the full article See related articles

Listed in

This article is not in any list yet, why not save it to one of your lists.
Log in to save this article

Abstract

The influence of annealing temperature on the chemical, structural, and electrophysical properties of porous OSG low-k films containing terminal methyl groups was investigated. The films were deposited via spin coating, followed by drying at 200 °C and annealing at temperatures ranging from 350 °C to 900 °C. In the temperature range of 350–450 °C, thermal degradation of surfactants occurs along with the formation of a silicon-oxygen framework, which is accompanied by an increase in pore radius from 1.2 nm to 1.5 nm. At 600–700 °C, complete destruction of methyl groups occurs, leading to the development of micropores. FTIR spectroscopy reveals that after annealing at 700 °C, the concentration of silanol groups and water reaches its maximum. By 900 °C, open porosity is no longer observed, and the film resembles dense SiO2. JV measurements show that the film annealed at 450 °C exhibits minimal leakage currents, approximately 5 × 10−11 A/cm2 at 700 kV/cm. This can be attributed to the near-complete removal of surfactant residues and non-condensed silanols, along with non-critical thermal degradation of methyl groups. Leakage current models obtained at various annealing temperatures suggest that the predominant charge carrier transfer mechanism is Poole–Frenkel emission.

Article activity feed