Tuning Optical Absorption and Device Performance in P3HT:PCBM Organic Solar Cells Using Annealed Silver Thin Films

In this study, we investigated the effect of annealing ultrathin silver (Ag) films of varying thicknesses (1–6 nm) on both their optical absorption and the performance of poly(3-hexylthiophene-2,5-diyl) (P3HT) and [6,6]-phenyl-C61-butyric acid methyl ester (PCBM) organic solar cells (OSCs). The Ag films were deposited on indium tin oxide (ITO) anodes and annealed at 300 °C for 1–2 hours to modify the anodic interface. The optical and electrical properties of the resulting devices were systematically characterized and optimized. The results revealed that a 1 nm AgO layer annealed for 2 hours significantly enhanced the device performance, yielding a 6% increase in power conversion efficiency compared to the standard configuration. This improvement is attributed to two main factors: (i) a 25% increase in light absorption of the AgO/P3HT:PCBM film due to localized surface plasmon resonance of Ag nanoparticles, and (ii) an 11% reduction in series resistance resulting from the favorable alignment of the Ag work function with the ITO anode and the polymer HOMO, which facilitates efficient hole extraction. These findings highlight the potential of ultrathin, annealed Ag/AgO interfacial layers as an effective strategy to enhance light absorption and charge transport in OSCs.